|Classification:||Chemical Auxiliary Agent||Appearance:||White Powder/Granule|
|Density:||0.98-1g/cm³||Viscosity:||11 000-22 000cps|
|Acid Value:||16-25mgKOH/g||Bulk Density:||About 600kg/m³|
|Valid Physical Content:||99.9%||CAS:||68441-17-8|
|Other Names:||OPE Wax,PE Wax,polyethylene Wax,polymer Wax||Application:||PVC Processing,PVC Products|
High Density Oxidized Polyethylene Wax OA9 With High Poftening Point And Good Hardness
Compared with PE Wax, The molecule structure of OPE Wax have some hydroxyl groups on them. So the intermiscibility with the polar resin will been improved a lot. It is better than PE wax when it is with the polar material such as rubber, plastic, paraffin. It is balance on PVC inside and outside lubrication. It is better than other lubricant when the OPE Wax used for hard and transparent PVC processing.
1. Non-toxic and non-irritating, high whiteness, without oligomer
2. High melting point, short melting process, low thermal weight loss and good thermal stability
3. Greatly improving the system fluidity, enhancing the processing performance and improving the production efficiency
4. Excellent lubricity and dispersity, improving the gloss of final products, no migration and no precipitation
|Physical form||White powder|
|Acid value (mgKOH/g)||18~22|
|Bulk density (kg/m³)||About 600|
Packing and Storage:
25kg/ Woven bag.
No decomposition at room temperature, but should be stored in a cool and dry place. Keep away from hot, fire source, avoid direct sunlight. Recommended storage and mixing areas have good ventilation conditions to avoid inhalation. Transportation according to the general chemicals.
Q1: Are you trading company or manufacturer?
A1: We are manufacturers in china for many years
Q2: How long is your delivery time?
A2: Within one week after receiving deposit.
Q3: Do you provide samples? is it free or extra?
A3: Yes we could offer the sample for free charge but you should pay the cost of freight
Q4: What is your terms of payment ?
A4: We support T/T,L/C and so on .