Product Details:
Payment & Shipping Terms:
|
Classification: | Chemical Auxiliary Agent | Appearance: | White Powder/Granule |
---|---|---|---|
Density: | 0.98-1g/cm³ | Viscosity: | 11 000-22 000cps |
Acid Value: | 16-25mgKOH/g | Bulk Density: | About 600kg/m³ |
Melt Point: | 138℃ | Color: | White |
Valid Physical Content: | 99.9% | Cas No.: | 68441-17-8 |
Type: | Processing Aid,Oxidized Polyethylene Wax,PE WAX | ||
High Light: | polyethylene wax powder,oxidised polyethylene wax |
Description
High-density oxidized polyethylene wax OA9 is an external lubricant and also has the function of internal lubricant. During the molding process, there are friction between molten polymer molecules and the surface of polymer melt and processing equipment. Friction, the former is called internal friction and the latter is called external friction. OA0 can effectively reduce external friction, improve the fluidity of plastic melt, prevent the adhesion of polymer materials to equipment during processing, and ensure the surface finish of products. Suitable for polyvinyl chloride, especially rigid polyvinyl chloride, polypropylene, polystyrene, polyamide, AFS resin, etc.
Product Specifications:
Physical form | White powder |
Density (kg/m³) | 970~1000 |
Viscosity (mm2/s) | 7000~10000 |
Penetration (dmm) | <1 |
Acid value (mgKOH/g) | 18~22 |
Bulk density (kg/m³) | About 600 |
Melting Point(℃) | 138 |
Applications:
Applied in the field of hot melt road marking material.
Act as the additive for shoeshine, floor wax, car wax, polishing wax, chinaware, pill wax, paint, coating, cable, carbon paper, wax paper, textile softening agent etc.
Our Services
1,Provide free sample for test and evaluation
2,Fast delivery and good customer service
3,Provide guideline and consulting service through your manufaturing process
Packing and Storage:
25kg/ Woven bag.
No decomposition at room temperature, but should be stored in a cool and dry place. Keep away from hot, fire source, avoid direct sunlight. Recommended storage and mixing areas have good ventilation conditions to avoid inhalation. Transportation according to the general chemicals.